Effect of Symmetric Alternating Current on Cathode Surface Before Iron Deposition

作  者:扈心坦 

机构地区:[1]大连海事大学镀铁研究所

出  处:《电化学》1995年第3期353-356,共4页ELECTROCHEMISTRY

Effect of Symmetric Alternating Current on Cathode Surface Before Iron Deposition

摘  要:研究了低碳钢在镀铁溶液内经对称交流电处理后在表面形成活化膜的组成及厚度,观察了镀铁层与基体界面的形貌,结果发现,活化膜的厚度随活化电流密度而变化,当电流密度为7Adm ̄(-2)时,在表面形成了一个厚度为20~25nm的洁净活化膜,镀铁层与基体结合牢固。探讨了对称交流电对阴极表面的作用机理。

The composition and thickness of active film formed on the surface of cathodemade of low carbon steel after treated by symmetric alternating current(SAC)in ferris chloride bathis studied,and the interfacial morphology of the iron deposit and the substrate is also examined.Theresults show that the active film,which a thickness of 20~25nm can be obtained under SAC densityof about 7A dm ̄(-2) ,so that the adherent iron deposit can be achieved on the active film. The effect ofSAC on cathode surface is discussed in detail.

关 键 词:镀铁 无刻蚀镀铁 对称交流电 活化膜 阴极表面 

Iron plating without anodic etching Symmetric alternating current Activation 

分 类 号:TQ153.19[化学工程—电化学工业]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关文献:

正在载入数据...

北京电子科技职业学院特色库 版权所有 ©2018