期刊 Evaluation of the Fitness of Glass-Infiltrated Zirconia Core in Maxillary Central Incisor  

作  者:Kim, Ji-Won[1]; Oh, Gye-Jeong[2]; Lim, Hyun-Pil[1]; Yun, Kwi-Dug[1]; Park, Chan[1]; Lee, Kyung-Ku[3]; Ban, Jae-Sam[3]; Park, Sang-Won[1]; Yim, Eun-Kyung[1]

机构地区:[1]Department of Prosthodontics, Dental Science Research Institute, School of Dentistry, Chonnam National University, Gwangju 61186, Republic of Korea [2]RIS Foundation for Advanced Biomaterials, School of Dentistry, Chonnam National University, Gwangju 61186, Republic of Korea [3]Bio-Medical Material and Component Service Center, Gwangju Technopark, Gwangju 61008, Republic of Korea

出  处:Journal of Nanoscience and Nanotechnology2018,18(2),1445-1448,4

语  种:外文

出 版 国:美国

摘  要:The purpose of this study was to evaluate the fitness of zirconia cores according to the amount and treated surface of glass infiltration. A maxillary right central incisor customized abutment was milled to have a 6�� slope and a 1 mm deep chamfer margin and was manufactured in an intaglio mold using silicone impression material. Fifty-six stone dies were produced by injecting high strength dental stone into a mold and then zirconia cores were milled with CAD/CAM systems. The control group (Control) used non glass-infiltrated zirconia, and the experiment group was divided by one with the glass and distilled water ratio of 1:300 and the other with the ratio of 1:100. Each group was divided into subgroups by glasstreated surface: external surface infiltration, internal surface infiltration, and both surface infiltration. The zirconia cores sintered after glass infiltration were attached to the stone dies and then cut. Afterwards, the absolute marginal discrepancies and internal gaps of the buccal and lingual sides were measured. The buccal absolute marginal discrepancies and lingual internal gaps were influenced by the glass infiltration amount (p < 0.05); while fitness of zirconia core were not affected by the glasstreated surface (p > 0.05). As a result of the above experiments, the glass-infiltrated zirconia cores showed a clinically acceptable fitness, which is within 120 ��m. This means that glass infiltration can be clinically used.

关 键 词:Fitness  Glass Infiltration  Zirconia 

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关文献:

正在载入数据...

北京电子科技职业学院特色库 版权所有 ©2018